La'ei ma le A'afiaga Fa'a'ave'ava'a La'ei La'ei Alumina Ceramic Rubber Pa'u La'ei
Fa'amatalaga
O le Conveyor Chute Wear Resistant Ceramic Rubber Liner o loʻo faia i luga ole alumina ceramics ma maualuga maualuga le paʻu natura faʻapipiʻiina e se faiga faʻapitoa.O mea sili ona lelei e faʻafefe ai le paʻu faʻanatura e fesoasoani e ausia ai se faʻalavelave faʻalavelave, ma puipuia ai le taʻe o taʻavale i le vaega maualuga o aʻafiaga, lea e sili atu lona aʻafiaga pe a faʻatusatusa i le sima faʻapipiʻi faʻapipiʻi saʻo i le fale uʻamea.A fa'atusatusa i le u'amea fa'afefete, o uiga o le Conveyor Chute Wear Resistant Ceramic Rubber Liner e sili atu ona tete'e i le ofuina ma le a'afiaga.O lo latou soifua tautua e sili atu le umi nai lo mea muamua e mafai ona fa'alavalava, ma e mafai ona tumau mo le tele o ta'amilosaga tapuni e aunoa ma le fa'atupuina tu'iga fa'alava po'o le fa'aletonu.
Meatotino tau vailaau
| S.Leai. | Meafaitino | Uiga | Meatotino |
| 1 | Tile Keramiki | Meafaitino | 92%, 95%, T95%,99%, ZTA,RBSIC |
| 2 | Papa | Vaega | pa'u fa'anatura, pa'u nitrile-butadiene, Fa'asa'o mū ,isi |
| Malosi | ~1.4g/cm3 | ||
| Malosi tete i le malepe | ≥15Mpa | ||
| Elongation i le malologa | ≥250% | ||
| Maaa o le matafaga | 45-65 | ||
| Fa'apipi'i i le va o le ta'ele ma le pa'u | 1.2-3.0 Mpa | ||
| Fa'apipi'i i le va o pa'u ma mea faigaluega | ≥3.8 Mpa | ||
| Fa'avevela vevela.(vevela masani) | 2w/m·k | ||
| Vaitaimi matua | ≥15 Tausaga | ||
| Galulue vevela | -50ºC - 200ºC | ||
| 3 | Papa u'amea | Meafaitino | Q235A |
| Malosi | 7.85g/cm3 | ||
| mafiafia | 5-6mm | ||
| 4 | Fa'apipi'i | Fa'aaliga | Suava fa'a'umi enaena |
| mea mautu | 20±3% | ||
| Viscosity | ≥2.5 Mpa | ||
| Pa'u malosi | 48h N/2.5cm≥120 | ||
| Malosi fa'amalosi | ≥850 Mpa | ||
| Galulue vevela | -20ºC - 100ºC |
Fa'aogaina o le Conveyor Chute Wear Resistant Ceramic Rubber Liner
O le Conveyor Chute Wear Resistant Ceramic Rubber Liner e tu'uina atu ie puipui mo meafaigaluega eseese, paipa, paipa, paipa, pefu, afa, mea e su'e ai mea faigaluega ma isi pisinisi.